Bearing manufacturing raw material bearing steel advantages

Bearing manufacturing raw material bearing steel advantages description bearing working condition monitoring and material performance requirements bearing combination structure design includes the following bearing materials bearing steel characteristics:

One. Contact fatigue strength

Under the action of periodic load, the contact surface of bearings is easily damaged, that is, the emergence of chapped peeling, which is an important failure situation of bearings. Therefore, in order to improve the service life of bearings, bearing steel must have high contact fatigue strength.

Two, wear resistance

When the bearing task, not only rolling friction, but also sliding friction will occur between the ring, the rolling body and the maintenance frame, so that the bearing parts have been worn. In order to increase the wear of bearing parts, maintain bearing accuracy stability, extend the service life, bearing steel should have good wear resistance.

Three, hardness

Hardness is one of the most important qualities of bearing quality, which has an indirect impact on contact fatigue strength, wear resistance and elastic limit. The hardness of bearing steel in use should individually reach HRC61~65, which enables the bearing to achieve higher contact fatigue strength and wear resistance.

Four, rust resistance

In order to avoid corrosion and rust of self-allocating roller bearing parts and finished products in the process of processing, storage and application, it is requested that bearing steel should have good antirust performance.

Five, processing performance

In the consumption process of bearing parts, there are many cold and hot processing procedures. In order to meet the requirements of a small amount, high efficiency and high quality, bearing steel should have good processing performance. For example, cold, hot forming performance, cutting performance, hardenability and so on.

In addition to the above basic requirements, bearing steel should also meet the requirements of appropriate chemical composition, average external tissue, less non-metallic dopants, conform to the specification of external appearance shortcomings, and the decarbonization layer on the surface does not exceed the regular concentration.